MIM Parts for Automotive Transmission

Finished Weight of Component :
Density (g/cm3) : 7.4 g/cm3
Tensile Strenght (N/mm2) : 450 MPa
Yield Strength (=0.2% N/mm2) :
Hardness : 500+250HV1
Treatment :
Description: All parts are made from iron-2% nickel powder sintered to a final density greater than 7.4 g/cm3. Tensile strength is put at 450 MPa; hardness is 500+250HV1.Three examples are shown here of metal injection moulded parts which have found applications in automotive transmission and help to synchronise the reverse gear

In the case of the braking disc (left) a special design feature is the tooth system.

Company:	(GKN Sintermetals GmbH)
	Dahlienstr 43, Radevormwald, D-42477 , Germany