Company Name:
Pacific Sintered Metals
Address: 14000 Avalon Boulevard Los Angeles, Ca 90061 USA
Tel: 310-715-9800
Fax: 310-715-1414
Contact: David Palombo, Sales Manager
Composition of PM Product: FC-0208 2% Copper Steel
Start Weight of Powder: 48 grams
Finished Weight of Component: 48 grams
Powder Consolidation Technique: Cold pressing
Consolidation Pressure: 35 tsi
Compact Denisty Before Sintering: 6.8 g/cc
Temperature for sintering or other method of hot consolidation:
2050°F
Final density of PM product (g/cm3): 6.7/6.8 g/cc
Percentage shrinkage from compact to final shape: +0.25%
(Growth)
Relative density as percentage of theoretical density: 87%
Further finishing operations: Oil dip
Density (g/cm3): 6.7/6.8:
Tensile Strength (N/mm2): 410
Yield Strength (=0.2% N/mm2): 380
Hardness: 70 RB
Elongation: <1.0%
Fatigue Endurance Limit (N/mm2): 160
Transverse Rupture Strength (N/mm2): 860
Poissons Ratio: 0.25
Youngs Modulus (KN/mm2): 120
Compressive Yield Strength (N/mm2): 340
Date PM Production First Started: 10/Mar/2004
Annual Production Quanity: 3,000,000
Unique tool concept and part complexity
|
|