ALUMINIUM BASED ALLOYS
Material r
g/cm3 		E
GPa 		Rm
MPa 		Rr0.2
MPa
(static) 		Hardness
HV5HRH		 A5
%
2014 2.50
2.64		 49
59 		150
180		 115
150		 . 70
75		 3
3
2014-T6 2.50
2.64		 49
59 		250
300		 235
280		 . 85
90		 1
2
6061 2.42
2.55		 47
56
100
125		 65
80		 62
65
 . 4
6
6061 - T6 2.42
2.55		 47
56 		140
210 		130
195		 72
.		 .
80
0.5
2
7075 2.51 49 205 150 90 . 3
7075 - T6 2.51 49 310 275 . 80 2


Notes:
All properties measured after sintering and sizing
T6 = solution hardening and artificial ageing

Date Source: E Mosca, Powder Metallurgy - Criteria for Design and Inspection, published in 'Guide to Design of Sintered Parts' and reprinted with permission of Assinter, Italy